Temperature and configurational effects on the Youngs modulus of poly (methyl methacrylate): a molecular dynamics study comparing the DREIDING, AMBER and OPLS force fields

Sahputra, Iwan Halim and Alexiadis, Alessio and Adams, Michael J. (2018) Temperature and configurational effects on the Youngs modulus of poly (methyl methacrylate): a molecular dynamics study comparing the DREIDING, AMBER and OPLS force fields. [UNSPECIFIED]

	PDF Download (880Kb)
	PDF Download (128Kb)
Preview	PDF (Paper - Iwan H) Download (2484Kb) | Preview
Preview	PDF (Cek plagiasi - Iwan H) Download (175Kb) | Preview
Preview	PDF (Peer review - Iwan H) Download (1205Kb) | Preview

Abstract

The effects of the configuration and temperature on the Youngs modulus of poly (methyl methacrylate) (PMMA) have been studied using molecular dynamics simulations. For the DREIDING force field under ambient temperatures, increasing the number of monomers significantly increases the modulus of isotactic and syndiotactic PMMA while the isotactic form has a greater modulus. The effects of temperature on the modulus of isotactic PMMA have been simulated using the DREIDING, AMBER, and OPLS force fields. All these force fields predict the effects of temperature on the modulus from 200 to 350 K that are in close agreement with experimental values, while at higher temperatures the moduli are greater than those measured. The glass transition temperature determined by the force fields, based on the variation of the modulus with temperature, is greater than the experimental values, but when obtained from a plot of the volume as a function of the temperature, there is closer agreement. The Youngs moduli calculated in this study are in closer agreement to the experimental data than those reported by previous simulations.

Actions (login required)